Aluminum and Small Multihulls

I always assume everybody knows that aluminum is not optimimal for efficient small multihulls.  I assume here that small is under 60′ length.  Still, it keeps coming up again.  And Bagalut was sweet.

internalspsp3

  There are many good reasons not to use aluminum for small multihulls. It starts to make sense when the catamarans are over about 50’ length. Smaller than that, it doesn’t make much sense in standard practice multihulls.

 Weight

 A typical composite 45’ catamaran in foam/glass would have hulls weighing between 1.1 and 1.3 lbs per square foot of hull.   Geoff Strange was doing infused hulls that weighed much less than that even.  

The same size aluminum cat would likely have 3/16” thick hulls weighing 2.65 lbs per sqft. Because the aluminum hulls are thinner than foam/glass ones, they need much more frequent internal structure than a composite hull. That adds significantly more weight and work again.

Even compared to an epoxy/plywood hull, again the aluminum is much heavier. A 45’ cat in plywood would typically have a 3/8” (10mm) thick hull that will weigh about 1.2 to 1.4 lbs per sqft.

In a recent study by Horsmon, a pair of nearly identical 135’ fast ferries, one in aluminum and the other composite, were compared   The composite version had a bare hull weight of 144,000 lbs or 65,454 kg. The aluminum bare hull to the same rule weighed 226,076 lbs or 102,762 kg. The composite hull had only 64% of the weight of the aluminum one.

 Thermal Insulation

Aluminum has very poor thermal insulating properties.   Of course composite gives very good insulation. In cold climates the air will easily condense on the aluminum hull causing moisture buildup inside. On a hot day, the metal hull can be like an oven.

The interior can be insulated, but that is another step, as below.

 Sound Insulation

Aluminum has very poor sound insulation properties. As expected, composite is an excellent sound insulator.

 Interior

The interior of an aluminum hull is a much more complicated project than with a composite one. It will need both stringers and frames. Unlike a composite hull where one has usually 6 or 8 feet of smooth surface, the insulation and maybe even the inside surface has to be fitted into the alloy structure. That covering must allow the aluminum to “breathe” so that it doesn’t set up a crevice corrosion situation.

 Unfair surfaces

An alloy hull typically distorts by the process of welding it together. Thinner, lighter hulls or those by a less skilled welder will be much more distorted. I understand that the surface of one of my 65’ daycharter cats in aluminum distorted up to a half inch as a result of the welding.

If the cat is to move well under sail or power, it must have fair hulls. To achieve that, the surface hollows must be filled with microbaloons and sanded.   That must then be coated and painted. It’s almost like putting a fiberglass hull over the aluminum hull. Typically, aluminum catamarans now are being built by former fish-boat builders. Hull fairness is not even a concept to them still. The solution to getting enough speed for them is to pile on more power, and they do that. Coming from racing catamarans, we know that only a smooth, fair hull can move easily at faster speeds.

 Hull Shape

An alloy hull must have a hard chine shape or be rolled into a rounded shape with a huge metal rolling machine. The hard chine is inconsistent with an easily driven displacement multihull. The rolling device is unavailable to many builders.

 Fatigue strength

The fatigue resistance of aluminum is not good. After some 5,000,000 use cycles (maybe 10 years), aluminum strength is about 1/5 of what it was in the beginning. Triaxial glass has about ¼ the strength it started with, but it started much higher. Plywood and carbon fiber will have about half the strength they began with, much better resistance to fatigue.

 Ultimate strength

According to ABS, the ultimate tensile strength of a 5000 series alloy will be between 31,000 lb and 42,000 lbs. That is the unwelded strength. The welded strength can be much less depending on alloy used.

A typical good backyard glass laminate will be about 60,000 psi in ultimate flexural strength and probably about 50,000 psi in ultimate tensile strength. Plywood will reach between 10,000 and 18,000 depending on species. The strength of aluminum is not as much as that of composite even though it is heavier.

 Toxic bottom paint.

Aluminum hulls cannot be painted with the usual copper based antifouling paint. That paint would rapidly corrode the aluminum hull. Instead, either the very expensive and toxic TBTF (tributln tin) bottom paints must be used, or the hull must be primed with an isolation paint first. The TBTF paints are toxic in parts per billion. Here in Washington state, they must be applied by a registered operator. The average owner cannot apply his own TBTF bottom paint. In many areas those paints are being banned.

 Lifetime costs

Corrosion is such a concern, that haulouts and inspections must be regular and the paint surface must be perfectly maintained. The lifetime costs will be higher than a composite boat. Randy Rust did part of article on this in an issue of Workboat. I will dig it up for the details.

 Ride

Even if they had the same hull shape, the composite hull affords a better ride.

Horsmon notes“The ride quality of the composite vessel will be superior to the aluminum vessel, although they share identical hull forms, because the composite vessel is compliant. The damping effect of the composite panels absorbs many of the short duration accelerations. These same accelerations are transmitted into the primary structure of an aluminum vessel. By the same token, machinery hull borne vibrations are decreased in composite vessels over stiff metallic construction.

Both shocks from hydrodynamic loading, and machinery initiated vibrations should be minimized in marine vessels to provide a comfortable ride to the passengers and prolong the service life of the vessel, as is evidenced in common fatigue studies.”

 Conclusion

In conclusion, for multihulls under perhaps 50’ length, an aluminum vessel is not appropriate.

It will be much heavier. Consequently, it will require much larger rig and engine to achieve the same speed as the same vessel in composite.

It will also require a composite structure to be built both outside of it to achieve the necessary fairness and maybe inside to create a livable space.

Over its lifetime it will cost more than the composite vessel.

7 thoughts on “Aluminum and Small Multihulls”

  1. Your article is interesting. Good luck beaching the composite boat and coming in hard to a wharf. The bit about having 1/5 the strength after time is unfounded. If you are not entering into the fatigue zone then it will lose no strength. Perhaps you should go and get an engineering degree too…

    1. you have a fishboat mentality. In that mentality a smooth hull is of no importance. the For an efficient multi, that is important. With any boat the problem with beaching is that the bottom paint goes away and the hull scratches. Both slow an efficient boat down. A fishboat doesn’t care and just adds more power.
      Fatigue strength of alum or any other materials has been documented for years.
      A Corecel/epoxy boat is surprisingly robust. And don’t forget F=MA. The composite multi will have about half the M.

  2. Hi Kurt:
    Horses for courses!
    Case 1- 55′ monohull in the tropics 86 degree water, 89 degree air. White painted decks. Air conditioning and generator. I’ll take an aluminum hull with 2 1/2 inches of spray foam (approximately r20 rating) over any cored hull anytime.
    Case II– summer voyage to Spitsbergen— same conclusion, cold instead of heat is the controlling factor.

    Fairness: The bare aluminum Garcia “Passion” that was in Seattle about 2O years ago. Round bilge shape developed on a giant roller by old man Garcia himself. Lightly framed with 12mm plating on the bottom and 9mm on the topsides. After being within 600 miles from the North Pole, around Cape Horn, and wintered in Sitka you could have shot Awlgrip on it with no fairing and had a yacht finish. Only achievable with a master builder and thick plating, but it certainly can be done.

    Still doesn’t mean one should build a multihull out of it!

    ps: I had a fun conversation with aluminum proponent John Harries in which I argued that a purpose designed multihull (composite of course!) would have several distinct advantages as a high latitude expedition vessel. The one reason he turned thumbs down on the idea was the difficulty of pushing ice aside as it becomes entrapped between the hulls.

  3. My cutoff point for purchasing of aluminum boats is 72 hours of continuous use and 30 feet length. As far as tenders and small fishing boats (Alumacraft, Yamaha, Niad etc) I’ll be damn if I don’t go aluminum. Aluminum is somewhat self healing in air and scratches and dents do not count that much. I had fiberglass, wood and aluminum tenders. Hands down aluminum is the best material.

    1. I understand, but it goes back to the baseline conditions wanted. You do not worry about a scratch or dent in the surface, you can just add more power to make up for it. I agree unless a smooth, fair surface is a design requirement.

  4. Spot on on all points but two:

    Insulation: Insulation does not have to be installed as individual panels held back from the metal to allow it to breathe. Crevice corrosion is a problem normally associated with stainless steel, not aluminum. Insulation can be sprayed directly on the bare metal. And the end result is a far better insulated hull than almost any cored composite simply because the insulation is thicker.

    Impact resistance:
    You failed to mention that aluminum (and steel) are ductile and as a result are much more resistant to damage from point impacts.

    If we were talking about monohulls with their heavier structures and thicker plating, I’d have to take exception to your comments about long term maintenance costs—- provided that you leave the hull unpainted. Thousands of Frenchmen have chosen bare aluminum because of its durability and low long term maintenance costs. And it would be my first choice for a monohull planning to sail the high latitudes.

    But, for all the other reasons you describe, aluminum (and of course steel) are not suitable for “small” multihulls— and I’d go even further and put the minimum size at 75′ and 100,000#.

    1. I appreciate your experience with alloy and insulation. Will look into more. I doubt if any more than R-5 is needed.
      Agree on the ductile. Again, unless baseline requirement is a smooth, fair surface.

Leave a Reply to Dan Cancel reply

Your email address will not be published. Required fields are marked *